The heat capacities and thermodynamic properties of NiAl2O4 and CoAl2O4 measured by adiabatic calorimetry from T = (4 to 400) K

Klemme, S., van Miltenburg, J. C.
J. Chem. Thermodyn. 2009, 41, 7, 842-848
ABSTRACT
The low-temperature heat capacity of NiAl2O4 and CoAl2O4 was measured between T = (4 and 400) K and thermodynamic functions were derived from the results. The measured heat-capacity curves show sharp anomalies peaking at around T = 7.5 K for NiAl2O4 and at T = 9 K for CoAl2O4. The exact cause of these anomalies is unknown. From our results, we suggest a standard entropy for NiAl2O4 at T = 298.15 K of (97.1 +- 0.2) J mol 1 K 1 and for CoAl2O4 of (100.3 +- 0.2) J mol 1 K 1.
Compounds
# Formula Name
1 Al2NiO4 aluminum nickel oxide
2 Al2CoO4 aluminium cobalt oxide
Datasets
The table above is generated from the ThermoML associated json file (link above). POMD and RXND refer to PureOrMixture and Reaction Datasets. The compound numbers are included in properties, variables, and phases, if specificied; the numbers refer to the table of compounds on the left.
Type Compound-# Property Variable Constraint Phase Method #Points
  • POMD
  • 1
  • Triple point temperature, K ; Crystal 2
  • Crystal 2
  • Crystal 1
  • Gas
  • Adiabatic calorimetry
  • 1
  • POMD
  • 1
  • Molar enthalpy of transition or fusion, kJ/mol ; Crystal 2
  • Crystal 2
  • Crystal 1
  • Gas
  • Adiabatic calorimetry
  • 1
  • POMD
  • 1
  • Molar heat capacity at constant pressure, J/K/mol ; Crystal 1
  • Temperature, K; Crystal 1
  • Pressure, kPa; Crystal 1
  • Crystal 1
  • Vacuum adiabatic calorimetry
  • 237
  • POMD
  • 1
  • Molar entropy, J/K/mol ; Crystal 1
  • Temperature, K; Crystal 1
  • Pressure, kPa; Crystal 1
  • Crystal 1
  • Vacuum adiabatic calorimetry
  • 40
  • POMD
  • 1
  • Molar heat capacity at constant pressure, J/K/mol ; Crystal 2
  • Temperature, K; Crystal 2
  • Pressure, kPa; Crystal 2
  • Crystal 2
  • Vacuum adiabatic calorimetry
  • 9
  • POMD
  • 1
  • Molar entropy, J/K/mol ; Crystal 2
  • Temperature, K; Crystal 2
  • Pressure, kPa; Crystal 2
  • Crystal 2
  • Vacuum adiabatic calorimetry
  • 1
  • POMD
  • 1
  • Molar heat capacity at constant pressure, J/K/mol ; Crystal 2
  • Temperature, K; Crystal 2
  • Pressure, kPa; Crystal 2
  • Crystal 2
  • Vacuum adiabatic calorimetry
  • 3
  • POMD
  • 1
  • Molar heat capacity at constant pressure, J/K/mol ; Crystal 1
  • Temperature, K; Crystal 1
  • Pressure, kPa; Crystal 1
  • Crystal 1
  • Vacuum adiabatic calorimetry
  • 42
  • POMD
  • 2
  • Triple point temperature, K ; Crystal 2
  • Crystal 2
  • Crystal 1
  • Gas
  • Adiabatic calorimetry
  • 1
  • POMD
  • 2
  • Molar enthalpy of transition or fusion, kJ/mol ; Crystal 2
  • Crystal 2
  • Crystal 1
  • Gas
  • Adiabatic calorimetry
  • 1
  • POMD
  • 2
  • Molar heat capacity at constant pressure, J/K/mol ; Crystal 1
  • Temperature, K; Crystal 1
  • Pressure, kPa; Crystal 1
  • Crystal 1
  • Vacuum adiabatic calorimetry
  • 290
  • POMD
  • 2
  • Molar entropy, J/K/mol ; Crystal 1
  • Temperature, K; Crystal 1
  • Pressure, kPa; Crystal 1
  • Crystal 1
  • Vacuum adiabatic calorimetry
  • 49
  • POMD
  • 2
  • Molar heat capacity at constant pressure, J/K/mol ; Crystal 2
  • Temperature, K; Crystal 2
  • Pressure, kPa; Crystal 2
  • Crystal 2
  • Vacuum adiabatic calorimetry
  • 24
  • POMD
  • 2
  • Molar heat capacity at constant pressure, J/K/mol ; Crystal 1
  • Temperature, K; Crystal 1
  • Pressure, kPa; Crystal 1
  • Crystal 1
  • Vacuum adiabatic calorimetry
  • 50
  • POMD
  • 2
  • Molar heat capacity at constant pressure, J/K/mol ; Crystal 2
  • Temperature, K; Crystal 2
  • Pressure, kPa; Crystal 2
  • Crystal 2
  • Vacuum adiabatic calorimetry
  • 4